Description
Hostalen CRP 100 black (XL) is a high density polyethylene (HDPE), black colored similar RAL 9004 with high melt viscosity particularly higher zero viscosity than standard compounds. Typical application: Extrusion of extra large and thick walled pipes to avoid the sagging of the melt and to maintain uniform wall thickness.
The product is classified as PE 100 and provides good stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.
Availability
Asia-Pacific, Australia and New Zealand, Europe, South & Central America
Typical Properties
Melt Flow Rate (190 °C/5.0 kg)
0.23 g/10 min
Melt Flow Rate (190 °C/21.6 kg)
6.4 g/10 min
Density
0.959 g/cm³
Flexural Creep Modulus (4-point loading / 2000 hr)
330 MPa
Tensile Modulus (23 °C)
1100 MPa
Tensile Stress at Yield (23 °C, 50 mm/min)
23 MPa
Tensile Strain at Break (23 °C)
650 %
Tensile Strain at Yield (23 °C, 50 mm/min)
8 %
MRS Classification
10 MPa
FNCT (4.0 MPa, 2% Arkopal N100, 80 °C)
>=1000 hr
Charpy Impact Strength - Notched (23 °C)
26 kJ/m²
Charpy Impact Strength - Notched (-30 °C)
13 kJ/m²
Shore Hardness (Shore D, 3 sec)
63
Vicat Softening Temperature (B50)
74 °C
Oxidation Induction Time (210 °C)
30 min
Carbon Black Content
2.25 %