Flame retardant Polyolefin compound with expandable graphite for extrusion and injection molding applications.
POLYFLAM RLD 7750
Description
Availability
Europe
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Volume Flow Rate (230 °C/21.6 kg) | 7.0 cm³/10 min |
| Density (Method A) | 1.24 g/cm³ |
| Tensile Modulus (1 mm/min, Type 1A) | 200 MPa |
| Tensile Stress at Yield (Type 1A, 50 mm/min) | 4.30 MPa |
| Tensile Strain at Yield (Type 1A, 50 mm/min) | 10 % |
| Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) | 35 kJ/m² |
| Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A) | 10 kJ/m² |
| Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) | No Break kJ/m² |
| Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise) | 28 kJ/m² |
| Shore Hardness (Shore A, 3 sec) | 26 |
| Vicat Softening Temperature (A (10N), 50 °C/h) | 61.0 °C |
| Deflection Temperature Under Load Unannealed (0.45 MPa) (Flatwise) | 45.0 °C |
| Deflection Temperature Under Load Unannealed (1.80 MPa) (Flatwise) | 33.0 °C |
| Surface Resistivity | >1.0E+14 ohm |
| Volume Resistivity | >1.0E+12 ohm*m |
| Comparative Tracking Index (CTI) | 600 V |
| Glow Wire Flammability Index (1.5 mm) | 960 °C |
| Glow Wire Ignition Temperature (1.5 mm) | 750 °C |
| Glow Wire Ignition Temperature (3.0 mm) | 750 °C |
| Drying Time | 2 hr |
| Drying Temperature | 70 °C |
| Processing (Melt) Temp | <170 °C |
| Mold Temperature | 40 °C |