Pro-fax 8523 very high impact polypropylene copolymer is available in pellet form. This resin is typically used in extrusion or injection molding applications and offers excellent low temperature impact resistance.
ASTM and ISO-based versions of the technical data sheet are available for Pro-fax 8523.
Pro-fax 8523
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 4.0 g/10 min |
| Density (23 °C) | 0.90 g/cm³ |
| Density (23 °C, Method A) | 0.90 g/cm³ |
| Flexural Modulus (23 °C) | 970 MPa |
| Flexural Modulus (0.05 in/min, 1% Secant, Procedure A) | 140000 psi |
| Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A) | 965 MPa |
| Tensile Strength at Yield (2 in/min) | 3100 psi |
| Tensile Strength at Yield (50 mm/min) | 21 MPa |
| Tensile Stress at Yield (23 °C) | 21 MPa |
| Tensile Elongation at Yield | 8 % |
| Tensile Strain at Yield (23 °C) | 9 % |
| Notched Izod Impact Strength (73 °F, Method A) | No Break ft-lb/in |
| Notched Izod Impact Strength (23 °C, Method A) | No Break J/m |
| Deflection Temperature Under Load (66 psi, Unannealed) | 165 °F |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 74 °C |
Process
Injection Molding, Sheet and Profile Extrusion
Resin
Polypropylene, Impact Copolymer
Applications
Automotive Parts