Pro-fax PH350
Description
Pro-fax PH350 general-purpose polypropylene homopolymer is available in spherical particle form. This resin has very minimal stabilization, which allows wide design latitude in compounding applications. Additional stabilization is required to protect the resin during melt processing and throughout its useful life.
Please note that any additives compounded into this resin will require a re-assessment of its FDA status.
Availability
North America
Product data and technical information
Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
3.5 g/10 min
Density (23 °C)
0.90 g/cm³
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
200000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
1380 MPa
Tensile Strength at Yield (2 in/min)
4800 psi
Tensile Strength at Yield (50 mm/min)
33 MPa
Tensile Elongation at Yield
12 %
Notched Izod Impact Strength (73 °F, Method A)
1.0 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
53 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
190 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
88 °C