Typical Properties
Melt Flow Rate (230 °C/2.16 kg)
8.0 g/10 min
Density (23 °C)
0.90 g/cm³
Density (23 °C, Method A)
0.90 g/cm³
Flexural Modulus (23 °C)
1130 MPa
Flexural Modulus (0.05 in/min, 1% Secant, Procedure A)
160000 psi
Flexural Modulus (1.3 mm/min, 1% Secant, Procedure A)
1100 MPa
Tensile Strength at Yield (2 in/min)
3700 psi
Tensile Strength at Yield (50 mm/min)
26 MPa
Tensile Stress at Yield (23 °C)
24 MPa
Tensile Elongation at Yield
8 %
Tensile Strain at Yield (23 °C)
9 %
Charpy Impact Strength - Notched (23 °C)
8.2 kJ/m²
Charpy Impact Strength - Notched (-40 °C)
1.9 kJ/m²
Notched Izod Impact Strength (23 °C)
7.4 kJ/m²
Notched Izod Impact Strength (-40 °C)
2.9 kJ/m²
Notched Izod Impact Strength (73 °F, Method A)
1.6 ft-lb/in
Notched Izod Impact Strength (23 °C, Method A)
85 J/m
Deflection Temperature Under Load (66 psi, Unannealed)
175 °F
Deflection Temperature Under Load (0.45 MPa, Unannealed)
72 °C
Deflection Temperature Under Load (0.45 MPa, Unannealed)
79 °C
Deflection Temperature Under Load (1.80 MPa, Unannealed)
48 °C