Polyphthalamid with 33% GF, high stiffness and strength at high temperatures, heatstabilzed, high chemical resistence
SCHULAMID PPA GF33 B200 BLK968001
Description
Availability
Europe
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Density (Method A) | 1.46 g/cm³ |
| Tensile Modulus (1 mm/min, Type 1A) | 13700 MPa |
| Tensile Modulus (1 mm/min, Type 1A) - Conditioned | 12000 MPa |
| Tensile Stress at Break (Type 1A, 5 mm/min) | 195 MPa |
| Tensile Stress at Break (Type 1A, 5 mm/min) - Conditioned | 162 MPa |
| Tensile Strain at Break (Type 1A, 5 mm/min) | 2.0 % |
| Tensile Strain at Break (Type 1A, 5 mm/min) - Conditioned | 1.6 % |
| Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) | 10 kJ/m² |
| Charpy Impact Strength - Notched (23 °C, Type 1, Edgewise, Notch A) - Conditioned | 10 kJ/m² |
| Charpy Impact Strength - Notched (-30 °C, Type 1, Edgewise, Notch A) | 10 kJ/m² |
| Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) | 70 kJ/m² |
| Charpy Impact Strength - Unnotched (23 °C, Type 1, Edgewise) - Conditioned | 37 kJ/m² |
| Charpy Impact Strength - Unnotched (-30 °C, Type 1, Edgewise) | 45 kJ/m² |
| Vicat Softening Temperature (B (50N)) | 303 °C |
| Deflection Temperature Under Load Annealed (0.45 MPa) (3.30 mm) | 297 °C |
| Deflection Temperature Under Load Annealed (1.80 MPa) (3.20 mm) | 285 °C |
| Deflection Temperature Under Load Unannealed (1.80 MPa) | 280 °C |
| Surface Resistivity | >1.0E+15 ohm |
| Surface Resistivity - Conditioned | >1.0E+12 ohm |
| Volume Resistivity | >1.0E+13 ohm*m |
| Volume Resistivity - Conditioned | >1.0E+10 ohm*m |
| Burning Rate (2.00 mm) | <100 mm/min |
| Burning Rate (2.00 mm) | <100 mm/min |
| Drying Time | 3.0 to 4.0 hr |
| Drying Temperature | 120 °C |
| Suggested Max Moisture | 0.040 to 0.10 % |
| Processing (Melt) Temp | 310 to 345 °C |
| Mold Temperature | 120 to 160 °C |
| Flammability Classification (1.5 mm) | HB |
| Flammability Classification (3.0 mm) | HB |